Mitigating grain growth in fully stabilized zirconia via a two-step sintering strategy for esthetic dental restorations [0.03%] 通过两步烧结策略降低全稳定氧化锆增材制造试样的晶粒长大速率用于美观的牙科修复体
Boo Kyung Kim,Jong Hyuk Yun,Wook Ki Jung et al. Boo Kyung Kim et al.
Overall, 8-mol% yttria-stabilized zirconia (8YSZ), unlike 3YSZ, is optically transparent and stable against low-temperature degradation but has insufficient mechanical properties due to its large grain size. The influence of the grain size ...
Effect of binder system on the thermophysical properties of 3D-printed zirconia ceramics [0.03%] 粘结系统对3D打印氧化锆陶瓷热物性的影响
Anna-Katharina Hofer,Julia Rabitsch,Dagmara Jutrzenka-Trzebiatowska et al. Anna-Katharina Hofer et al.
Fabrication of 3D-printed ceramic parts with high complexity and high spatial resolution often demands low wall thickness as well as high stiffness at the green state, whereas printing simpler geometries may tolerate thicker, more compliant...
Determination of silicon carbide fiber electrical resistivity at elevated temperature [0.03%] 高温下碳化硅纤维电阻率的测定
Craig Smith,Greg Morscher Craig Smith
The resistance of Sylramic-iBN and Hi-Nicalon SiC fiber tows was measured at elevated temperature in air. Resistivity could not be directly measured, since the fibers passed through a furnace with varying temperature along the length. The r...