Phase equilibria and microstructural evolution in ternary Co-Al-W between 750 °C and 1100 °C [0.03%]
三元Co-Al-W系750℃~1100℃平衡与组织演变研究
Eric A Lass,Richard D Grist,Maureen E Williams
Eric A Lass
Phase equilibria between 750 °C and 1100 °C in the Co-rich portion of the Co-Al-W ternary system are investigated via isothermal annealing of five ternary alloy compositions. At temperatures of 900 °C and below, the phase diagram is domi...
Microstructure and Electro-Physical Properties of Sn-3.0Ag-0.5Cu Nanocomposite Solder Reinforced with Ni Nanoparticles in the Melting-Solidification Temperature Range [0.03%]
Ni纳米粒子增强Sn-3.0Ag-0.5Cu纳米复合焊料的熔融-凝固温度范围内的微观结构和电物理性能
A Yakymovych,Yu Plevachuk,V Sklyarchuk et al.
A Yakymovych et al.
The electrical conductivity of nanocomposite Sn-3.0Ag-0.5Cu alloys with two different weight percentages of Ni nanoparticles (1.0 and 2.0 wt.%) was measured over a wide temperature range. The samples were produced using a cold pressing meth...
Peter Kainzbauer,Klaus W Richter,Herbert Ipser
Peter Kainzbauer
The binary bismuth-rhodium (Bi-Rh) phase diagram was reinvestigated from 23 to 60 at.% Rh with focus on the BiRh phase, applying powder-x-ray diffraction (XRD), high temperature powder-XRD, differential thermal analyses and scanning electro...
William J Boettinger
William J Boettinger
Various topics taken from the author's research portfolio that involve multicomponent alloy solidification are reviewed. Topics include: ternary eutectic solidification and Scheil-Gulliver paths in ternary systems. A case study of the solid...
Ursula R Kattner
Ursula R Kattner
Enthalpies of Formation of (Cu,Ni)3Sn, (Cu,Ni)6Sn5-HT and (Ni,Cu)3Sn2-HT [0.03%]
(Cu,Ni)3Sn、(Cu,Ni)6Sn5-HT和(Ni,Cu)3Sn2-HT的生成焓
C Schmetterer,M Rodriguez-Hortala,H Flandorfer
C Schmetterer
Standard enthalpies of formation of ternary phases in the Cu-Ni-Sn system were determined along sections at 25, 41 and 45.5 at.% Sn applying tin solution drop calorimetry. Generally, the interaction of Ni with Sn is much stronger than that ...
Yu Plevachuk,A Yakymovych,S Fürtauer et al.
Yu Plevachuk et al.
The partial and integral enthalpies of mixing of liquid ternary Ni-Sn-Zn alloys were determined. The system was investigated along two sections xNi/xSn ≈ 1:9, xNi/xSn ≈ 1:6 at 1073 K and along two sections xSn/xZn ≈ 9:1, xSn/xZn ≈ 4:1 a...