Influence of different curing modes on the bonding effectiveness of self-adhesive resin luting cements in combination with universal adhesives [0.03%]
不同固化模式对通用型黏合剂与自粘接树脂黏固剂黏结效果的影响
Ryota Aoki,Toshiki Takamizawa,Kana Hayashi et al.
Ryota Aoki et al.
Objectives: This study aimed to investigate the immediate dentin bond performance and bond durability of self-adhesive resin luting cements (RLCs) in combination with universal adhesives in different curing modes. ...
Effect of firing time and wall thickness on the biaxial flexural strength of 3D-printed zirconia [0.03%]
烧结时间和壁厚对3D打印氧化锆的双轴弯曲强度的影响
Stefan Rues,Christopher Herpel,Ali Ilani et al.
Stefan Rues et al.
Objectives: To evaluate the effect of accelerated firing on 3D-printed zirconia. Methods: To check if formulae provided by ISO 6872 can...
Shear bond strength between standard or modified zirconia surfaces and two resin cements incorporating or not 10-MDP in their matrix [0.03%]
标准或改性氧化锆表面与两种树脂水泥（包含或不包含10-MDP）之间的剪切粘结强度研究
Roman Tatiana,Cournault Bérangère,Teyagirwa Prudence Felix et al.
Roman Tatiana et al.
Objective: This study aimed first to compare the shear bond strength between zirconia samples luted to enamel with a 10-MDP- containing resin cement (Panavia F2.0, Kuraray, Japan) and those luted with a resin cement using...
Borosilicate glass as a surface finishing alternative for improving the mechanical properties of third-generation zirconia [0.03%]
硼硅酸盐玻璃作为提高第三代氧化锆的机械性能的表面处理方法的选择
Camila da Silva Rodrigues,Ana Carolina da Silva,Clarice Ferreira Sabino et al.
Camila da Silva Rodrigues et al.
Objective: This study evaluated the effect of an experimental borosilicate glass on the mechanical and optical behavior of 5Y-PSZ zirconia and comparing it to commercial glaze and as-sintered. ...
Tooth-composite bond failure with a universal and an etch-and-rinse adhesive depending on mode and frequency of application [0.03%]
通用粘接剂和蚀刻冲洗型粘接剂的牙体-树脂结合强度失败依赖于应用方式和频率
Ellen Schulz-Kornas,Mathilde Tittel,Hartmut Schneider et al.
Ellen Schulz-Kornas et al.
Objectives: To evaluate the effect of an additional layer of universal adhesive on the interfacial enamel/dentin-composite gap formation in relation to application mode and aging, via spectral domain optical coherence tom...
Influence of surface sealants on the quality of posterior restorations with bulk-fill composites: A 4-year randomized clinical trial [0.03%]
表面密封剂对大块填复合材料后牙修复质量的影响:一项4年的随机临床试验
Fernanda Signorelli Calazans,Thárcila de Medeiros Jabor Ferreira,Romina Ñaupari-Villasante et al.
Fernanda Signorelli Calazans et al.
Objectives: The aim of this study was to evaluate the clinical performance of surface sealants associated with a bulk-fill composite in posterior restorations after 4 years. ...
Randomized Controlled Trial
Dental materials : official publication of the Academy of Dental Materials. 2024 Mar;40(3):466-476. DOI:10.1016/j.dental.2023.12.011 2024
Microbiological, physicomechanical, and surface evaluation of an experimental self-curing acrylic resin containing halloysite nanotubes doped with chlorhexidine [0.03%]
含有载氯己定埃洛石纳米管的实验自固化丙烯酸树脂的微生物学，物理机械和表面性质评估
Isabelle C G Timbó,Mayara S C S Oliveira,Ramille A Lima et al.
Isabelle C G Timbó et al.
Objective: The objective was to synthesize halloysite nanotubes loaded with chlorhexidine (HNT/CHX) and evaluate the antimicrobial activity, microhardness, color change, and surface characteristics of an experimental self...
Effects of solvent type and UV post-cure time on 3D-printed restorative polymers [0.03%]
溶剂类型和紫外后期固化时间对3D打印修复聚合物的影响
Nathalia S Finck,May Anny A Fraga,Américo B Correr et al.
Nathalia S Finck et al.
Objectives: This study evaluated the impact of different solvents and UV post-curing times on properties of 3D printing resins for provisional restorations. ...
Temperature rise in photopolymerized adhesively-bonded resin composite: A thermography study [0.03%]
光固化粘接树脂复合材料中的温度上升：热成像研究
Hamad Algamaiah,Jiawei Yang,Abdulaziz Alayed et al.
Hamad Algamaiah et al.
Objectives: To assess visually and quantitatively the contributions of the adhesive layer photopolymerization and the subsequent resin composite increment to spatio-temporal maps of temperature at five different cavity lo...
Properties of model E-glass fiber composites with varying matrix monomer ratios [0.03%]
不同基体单体配比的E-玻璃纤维复合材料性能研究
Abdulrahman Alshabib,Nikolaos Silikas,David C Watts
Abdulrahman Alshabib
Objective: To evaluate properties of fiber-reinforced-composites (FRC) containing Bis-EMA/UDMA monomers but identical dispersed phase (60% wt BaSi glass power +10% wt E-glass fibre). ...