Hydrogen-Induced Cracking Susceptibility of API 5L X100 Steel Welded Joint
{{output}}
Hydrogen-induced cracking (HIC) is a possible failure mode of high-strength pipeline steel welded joints. The HIC susceptibility of shielded metal arc-welded joint of X100 pipeline steel was investigated using the slow strain rate tensile test (SSRT) under cur... ...